It’s based on epoxy resin and polyamide hardener. It has very high permeability and permeates deep into the concrete, due to its low viscosity. It has high adhesion to concrete surface and prevent exiting dust of concrete pores. Very good water and chemical resistance. The surface of this coating is washable and resistant against chemicals and detergents.
- Very low viscosity
- Excellent permeation capability in concrete pores
- Prevent exiting dust of concrete pores and environmental pollution Covering surface imperfections of concrete
- Increase abrasion resistance
- Protects concrete against chemicals, such as: acids, alkalis, gasoline, petroleum, petrol…
Main uses :
- Anti-Dust floorings on the concrete/brick/cement…surfaces where it is not expose to direct sunlight
|Gray, dark blue and any color ordered
|Mixing Ratio by weight
|Mixing Ratio by volume
|4.5 hours @ 5°c
3 hours @ 25°c
2.5 hours @ 35°c
|% solid volume (A+B)
|400 g/ m2
For 200 Micron
|Solvent vaporization and Chemical reaction
|T-950 Epoxy thinner
In closed containers , not exposed to direct sun light in 5-30ºc
|A: 8 Kg
B: 4 Kg
|Dust free time
|Post curing time
|Full curing time
|Over coating interval
Application Guide Direction:
The surface should be free of any contamination and loos area, because this material decrease adhesion between coating and surface. If the surface need to repair do it before flooring. In case of high surface absorption, apply PFEP-2168 POLYGUM concrete Epoxy primer. The coating can be applied in multilayers if necessary.
Ambient temperature while application should be between 5- 50ºc. The ambient temperature should be 3˚C more than dew point.
After surface preparation, Mix 2components (according instruction of packaging) with agitator until a homogenous liquid achieves. Pour the mined compound on the floor and spread it with trowel or roller. In closed area air conditioning during operation time is necessary.
After application clean the tools with Epoxy thinner T-950.
Please note PFEP –۲۱۵۰ is not suitable for wet and oil contaminated concrete surfaces.